C36000 Free Machining Brass Specification Sheet

Specifications Sheets

Chemical Composition
(%max., unless shown as range or min.)

  Cu Fe Pb Zn
Min./Max. 60.0-63.0 .35 2.5-3.0 Rem.
Nominal 61.5 - 2.7 35.4

Mechanical Properties (measured at room temperature, 68 F (20 C)

Temper Section
Size		 Cold
Work		 Typ/
Min		 Temp Tensile
Strength		 Yield
Strength
(0.5% ext.
under load)		     El Rockwell
Hardness		   Brinell
Hard.		 Shear
Strength		 Fatigue
Strength*		  
  in. %   F ksi ksi     % B C F 30T   500 3000 ksi ksi  
  mm.     C MPa MPa                     MPa MPa  
Rod
H04 0.375 0 TYP 68 - -     - 78 - - -   - - 34 -  
  12.7     20 - -     - 78 - - -   - - 234 -  
H02 1.5 0 TYP 68 - -     - 65 - - -   - - - -  
  38.1     20 - -     - 65 - - -   - - - -  
H04 0.625 0 SMIN 68 65 30     6 - - - -   - - - -  
  15.9     20 450 205     6 - - - -   - - - -  
H02 3.0 0 SMIN 68 45 15     20 - - - -   - - - -  
  76.2     20 310 105     20 - - - -   - - - -  
O60 1.5 0 SMIN 68 44 18     20 - - - -   - - - -  
  38.1     20 305 18     20 - - - -   - - - -  
H02 0.75 0 MIN 68 - -     - 70 - - -   - - - -  
  19.1     20 - -     - 70 - - -   - - - -  
H02 <0.50 0 TYP 68 - -     - 65 - - -   - - 32 20  
  12.7     20 - -     - 65 - - -   - - 221 138  
Bar
H02 <0.50 0 SMIN 68 50 25     10 - - - -   - - - -  
  <12.7     20 345 170     10 - - - -   - - - -  
O60 1.5 0 SMIN 68 40 15     25 - - - -   - - - -  
  38.1     20 275 105     25 - - - -   - - - -  
Shapes
H01 0.5 11 TYP 68 56 45     20 62 - - -   - - 33 -  
  12.7     20 386 310     20 62 - - -   - - 228 -  
M30 0.5 0 TYP 68 49 18     50 - - 68 -   - - 30 -  
  12.7     20 338 124     50 - - 68 -   - - 207 -  
Rod
H02 1.5 0 SMIN 68 50 20     15 - - - -   - - - -  
  38.1     20 345 140     15 - - - -   - - - -  
O60 <1 0 SMIN 68 48 20     15 - - - -   - - - -  
  <25.4     20 330 124     15 - - - -   - - - -  
Bar
H02 1.5 0 TYP 68 - -     - 60 - - -   - - - -  
  38.1     20 - -     - 60 - - -   - - - -  
H02 <0.50 0 TYP 68 - -     - 65 - - -   - - - -  
  <12.7     20 - -     - 65 - - -   - - - -  
Rod
H02 4.5 0 SMIN 68 40 15     20 25 - - -   - - - -  
  114.3     20 275 105     20 25 - - -   - - - -  
H04 0.25 0 TYP 68 - -     - 80 - - -   - - 38 -  
  6.35     20 - -     - 80 - - -   - - 262 -  
Flat Products
H02 0.25 11 TYP 68 56 45     20 62 - - -   - - 33 -  
  4.76     20 386 310     20 62 - - -   - - 228 -  
Rod
H04 0.375 0 SMIN 68 70 35     4 - - - -   - - - -  
  12.7     20 480 240     4 - - - -   - - - -  
H02 0.75 0 SMIN 68 55 25     10 - - - -   - - 34 -  
  19.1     20 380 170     10 - - - -   - - 234 -  
H02 3.0 0 TYP 68 - -     - 55 - - -   - - - -  
  76.2     20 - -     - 55 - - -   - - - -  
Bar
O60 <1 0 SMIN 68 44 18     20 - - - -   - - - -  
  <25.4     20 305 125     20 - - - -   - - - -  
Rod
O60 <1 0 TYP 68 - -     - 28 - - -   - - 30 -  
  <25.4     20 - -     - 28 - - -   - - 207 -  
H04 0.25 0 SMIN 68 80 45     - - - - -   - - - -  
  6.35     20 550 310     - - - - -   - - - -  
O60 2.5 0 SMIN 68 40 15     25 - - - -   - - - -  
  63.5     20 40 15     25 - - - -   - - - -  
H02 <0.50 0 TYP 68 57 25     7 - - - -   - - - -  
  12.7     20 395 170     7 - - - -   - - - -  
Bar
H02 3 0 SMIN 68 40 15     20 - - - -   - - - -  
  76.2     20 275 105     20 - - - -   - - - -  
H02 1.5 0 SMIN 68 45 17     15 - - - -   - - - -  
  38.1     20 310 115     15 - - - -   - - - -  
O60 1.5 0 TYP 68 - -     - 22 - - -   - - - -  
  38.1     20 - -     - 22 - - -   - - - -